TCE625+
Ultra-durable protection for extreme industrial environments
TCE625+ is an advanced EHLA (Extreme High‑Speed Laser Application) coating developed by Technoplating Group. This state‑of‑the‑art layer delivers exceptional wear, corrosion and impact resistance even in the harshest conditions. Because it’s metallurgically bonded to the base material, the coating will not peel or delaminate, extending the service life of critical components far beyond conventional solutions.
An evolved version of Inconel 625
Can be compared to Inconel 625 in performance, TCE625+ is based on a completely different advanced powder formulation engineered for superior results.
This unique composition combined with the EHLA process creates a denser, tougher and longer‑lasting coating than traditional solution. Delivering wear and corrosion resistance that surpasses Inconel 625, while maintaining excellent ductility and toughness.
Benefits of TCE625+
​
TCE625+ offers a range of key advantages, with its exceptional corrosion resistance and exceptional wear resistance standing out as the most important benefits.
Extreme Durability
The coating creates an exceptionally tough barrier which greatly increases the service life of critical components.
​
Outstanding Corrosion Resistance
TCE625+ shields the base material from harsh environments, offering long‑term protection against rust and chemicals
​
Superior Wear Resistance
The layer prevents abrasion, galling and surface damage even under heavy mechanical loads
​
Strong Metallurgical Bonding
Because the layer fuses with the base material, it won’t peel or flake — even when exposed to vibration or impact.
​
Maintains Mechanical Properties
Despite the increased hardness and corrosion resistance of the coating it maintains its flexibility and impact resistance, preventing cracking under stress.
​
Specification
Value
Hardness (HV)
450 HV
Hardness (HRC)
45 HRC
Rockwell indentation
No cracking around indentation
Bonding strength
Infinite (metallurgic bonding)
Elasticity and Ductility
Excellent
Heat Affected Zone (HAZ)
<5% of layer thickness
+++++ (5 of 5)
1.65 (65% increase)
33 volume loss/mm³
+++++ (5 of 5)
No corrosion after > 4200hr
< 0%
No visible corrosion
Layer cracks
No cracks
Wear score
ASTM-G65A
ASTM-G65B
Corrosion score
Saline droplet test
Porosity
Destructive porosity
Capacity
EHLA Laser Cladding
Ø1000 x 15.000mm
20.000kg